Series V530
Omnithane
This product has been discontinued. Please contact your local sales representative for further assistance.
Generic Type
Moisture-Cured Aromatic Urethane
Common Usage
Aluminum pigmented primer or finish for marginally cleaned steel. Provides excellent abrasion-, moisture-, chemical- and corrosion-resistance. Suitable for use as a topcoat where an aluminum finish is desired. Topcoating provides enhancement of systems and more latitude with color. Compatible with aged coatings, but verify with test patch.
Colors
Aluminum
Finish
Matte
Theoretical Coverage
818 mil sq ft/gal (20.1 m²/L at 25 microns). See APPLICATION for coverage rates.
Recommended DFT
2.0 to 3.0 mils (50 to 75 microns) per coat. Caution: Application at film thicknesses exceeding 3.0 dry mils (75 microns) per coat or at relative humidities above 70% R.H. may cause bubbles to form in the cured film.
Volatile Organic Compounds
Unthinned: 1.25 lbs/gallon (149 grams/litre)
Curing Time
Temperature † | To Touch | To Handle | To Recoat |
---|---|---|---|
75°F (24°C) | 2 hours | 3 hours | 5 hours |
† 50% Relative Humidity
Curing time varies with surface temperature, air movement, humidity and film thickness.
Note: For faster curing, low humidity and low-temperature applications, add No. 44-710 Urethane Accelerator; see separate product data sheet.
Number of Components
One
Topcoats
Series 2H, 2HS, 27, 66, 66HS, L69, N69, 72, 73, 82HS, 113, 114, 161, 161HS, V530, 1028, 1029, 1074, 1074U, 1075, 1075U, 1077
Note: Series V530 exterior (sunlight) exposed for 24 hours or longer requires scarification or an intermediate coat of Series 27, 66, 66HS or N69 prior to topcoating with itself (V530), 72, 73, 1028, 1029, 1074, 1074U, 1075, 1075U or 1077. Also if exterior exposed for 7 days or longer, V530 requires scarification or an intermediate coat of 27, 66, 66HS or N69 prior to topcoating with 113 or 114. The intermediate coat color should be noticeably different but in the same family as the specified topcoat color.
HAPS
Unthinned: 0.03 lbs/gal solids
Volume Solids
51.0 ± 2.0%