||Versatile epoxy coating (factory accelerated version of L140) for protection and finishing of steel. It has excellent resistance to abrasion and is suitable for immersion service. This product can be used for lining storage tanks that contain demineralized, deionized or distilled water.
||1255 Beige, 1211 Red, 15BL Tank White. Note: Epoxies chalk with extended exposure to sunlight. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause yellowing to occur.
||Self-priming, 1, 91-H2O, 94-H2O, N140, N140F, L140, V140, V140F, 141
||Interior: Series 22, FC22, L140, L140F, N140, N140F, V140, V140F, 141
Exterior: Series 27, 66, L69, L69F, N69, N69F, V69, V69F, 72, 73, L140, L140F, N140, N140F, V140, V140F, 156, 157, 161, 175, 180, 181, 446, 740, 750, 1028, 1029, 1074, 1074U, 1075, 1075U, 1080, 1081. Refer to COLORS on applicable topcoat data sheets for additional information. Note: The following recoat times apply for Series L140F: Immersion Service—Surface must be scarified after 30 days. Atmospheric Service—After 30 days, scarification or an epoxy tie-coat is required. When topcoating with Series 740 or 750, recoat time for L140F is 14 days. Contact your Tnemec representative for specific recommendations.
||66.0 ± 2.0% (mixed) †
||2.0 to 10.0 mils (50 to 255 microns) per coat. Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.
|Volatile Organic Compounds
||Unthinned: 0.79 lbs/gallon (95 grams/litre)
Thinned 5% (No. 49 Thinner): 0.79 lbs/gallon (95 grams/litre) †
||Unthinned: 0 lbs/gal solids
Thinned 5% (No. 49 Thinner): 0 lbs/gal solids
||1,059 mil sq ft/gal (26.0 m²/L at 25 microns). See APPLICATION for coverage rates. †
|Number of Components
||Two: Part A (amine) and Part B (epoxy) — One (Part A) to one (Part B) by volume.