||Innovative potable water coating which offers high-build edge protection and allows for application at a wide range of temperatures (down to 35°F or 2°C). For use on the interior and exterior of steel or concrete tanks, reservoirs, pipes, valves, pumps and equipment in potable water service.
||1211 Red, 1255 Beige, 00WH Tnemec White, 15BL Tank White, 39BL Delft Blue, 35GR Black. Note: Epoxies chalk with extended exposure to sunlight. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause yellowing to occur.
||215, 217, 218
||Self-priming, 22, 91-H2O, 94-H2O, L140, L140F, N140, V140, 141
||Interior: Series 22, FC22, L140, L140F, N140, N140F, V140, V140F, 141, 406
Exterior: Series 27, 66, L69, L69F, N69, N69F, V69, V69F, 72, 73, L140, L140F, N140, N140F, V140, V140F, 156, 157, 161, 175, 180, 181, 446, 740, 750, 1028, 1029, 1074, 1074U, 1075, 1075U, 1077, 1078, 1080, 1081. Refer to COLORS on applicable topcoat data sheets for additional information. Note: The following recoat times apply for Series N140F: Immersion Service—Surface must be scarified by blasting with fine abrasive after 30 days. Atmospheric Service—After 30 days, scarification or an epoxy tie-coat is required. When topcoating with Series 740 or 750, recoat time for N140F is 14 days. Contact your Tnemec representative for specific recommendations.
||68.0 ± 2.0% (mixed) †
||2.0 to 10.0 mils (50 to 225 microns) per coat. Note: MIL-PRF-4556F applications require two coats at 4.0-6.0 mils (100-150 microns) per coat. Otherwise, the number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.
|Volatile Organic Compounds
||Unthinned: 2.3 lbs/gallon (273 grams/litre)
Thinned 5% (#60): 2.5 lbs/gallon (299 grams/litre)
Thinned 10% (#4): 2.7 lbs/gallon (323 grams/litre) †
||Unthinned: 2.3 lbs/gal solids
Thinned 5% (#60): 2.3 lbs/gal solids
Thinned 10% (#4): 3.1 lbs/gal solids
||1,094 mil sq ft/gal (26.8 m²/L at 25 microns). See APPLICATION for coverage rates. †
|Number of Components
||Two: Part A (amine) and Part B (epoxy) — One (Part A) to one (Part B) by volume.