||Modified Polyamine Epoxy
||An advanced generation, 100% solids epoxy liner for the protection of steel and concrete. It provides excellent resistance to abrasion and is suitable for immersion and chemical contact. For use on the interior and exterior of steel or concrete tanks, reservoirs, and pipes in potable water service.
||WH08 White. Note: Epoxies chalk with extended exposure to sunlight. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause yellowing to occur.
||Series 215, 218
||Self-priming or Series 1, 91-H2O, 94-H2O, L140, L140F, N140, N140F, V140, V140F
||16.0 to 40.0 mils (405 to 1015 microns) in a one coat application. Note: Thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.
Note: These times are based on a 20.0 mil (500 micron) dry film thickness. Curing time varies with surface temperature, air movement, humidity and film thickness. Ventilation: When used as a tank lining or in enclosed areas, provide adequate ventilation during application and cure.
|Temperature||To Handle||Max to Recoat||Immersion|
|110°F (43°C)||1 hour||7 days||16 hours|
|75°F (24°C)||6 hours||7 days||24 hours|
|35°F (2°C)||12 hours||7 days||48 hours|
|Volatile Organic Compounds
||EPA Method 24 Unthinned: 0.04 lbs/gallon (5 grams/litre)
||1,604 mil sq ft/gal (39.4 m²/L at 25 microns.) See APPLICATION for coverage rates.
|Number of Components
||Two: 1 (Part A amine) to 2 (Part B epoxy)