||Waterborne Epoxy-Amine Adduct
||A low odor, rapid cure, wear-resistant coating for floors, walls and other substrates, capable of withstanding moderate commercial and industrial environments. It can withstand mild to moderate chemical and solvent exposures, as well as repeated cleaning. Can also be used as a primer or intermediate coat for thin film epoxy and urethane and acrylic systems.
||Available in clear and the 16 standard StrataShield colors. Special colors available, please contact your Tnemec representative. Note: Epoxies chalk and yellow with age, extended exposure to UV and artificial lighting. Caution should be taken when selecting white and light pastel colors. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause amine blush, possibly affecting adhesion of subsequent topcoats.
||Series 130, 215, 218, 1254. Note: A repair kit of 201, with Part C fumed silca, is available for small patching/surfacing repairs. For more extensive repairs and additional information, contact your Tnemec representative or Tnemec Technical Services.
||Concrete: Self-priming or Series 27WB, 201, 203, 205
CMU: Self-priming over filled CMU
Wood & Drywall: Self-priming or Series 201, 203
||Series 73, 280, 290, 291, 294, 295, 296, 297, 1074, 1075, 1080, 1081
||51.0 ± 2.0% (mixed) †
||Horizontal: 2.0 to 4.0 mils (50 to 100 microns) per coat. (Apply minimum of 2 coats to unpainted floors.)
Vertical: 2.0 to 3.0 mils (50 to 75 microns) per coat.
• 50% relative humidity. Curing time varies with surface temperature, air movement, humidity and film thickness.
|Temperature • || To Topcoat || To Place in Service|
| 60°F (16°C) || 6-7 hours || 8-10 hours |
| 75°F (24°C) || 4-5 hours || 7-8 hours |
| 85°F (29°C) || 1 1/2-3 hours || 4-6 hours |
|Volatile Organic Compounds
||Unthinned: 0.05 lbs/gallon (6 grams/litre)
Thinned 5% (Water): 0.05 lbs/gallon (6 grams/litre) †
||818 mil sq ft/gal (20.1 m²/L at 25 microns). See APPLICATION for coverage rates. †
|Number of Components
||Two: Part A (epoxy) and Part B (amine) — 2 Parts A to 1 Part B by volume