||A fiberglass mat reinforced coatings system for walls and ceilings providing cleanability and protection against chemical and physical abuse. Provides a high-performance, smooth, seamless surface with excellent chemical, stain, impact and abrasion resistance.
||15BR Pale. Note: Epoxies chalk and yellow with age, extended exposure to UV and artificial lighting. Caution should be taken when selecting white and light pastel colors. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause amine blush, possibly affecting adhesion of subsequent topcoats.
||CMU, Concrete & Cement Board: Series 215 or 218. Series 201 or 273 mixed with fumed silica (refer to Technical Bulletin 98-11). Note: Series 215 can also be used as a bedding coat for Series 273 Stranlok ML system. Refer to the applicable product data sheet for additional information.
||Wall Board, Wood & Drywall: Self-priming or Series 27WB, 151, 201, 233
Note For taping joints on drywall, use a high quality taping compound such as Sheetrock brand Durabond 90.
||Series 22, 27WB, 73, 113, 114, 280, 280FC, 282, 287, 290, 297, 1074, 1075, 1080, 1081. Note: Series 273 saturant coat must be topcoated with 22, 27WB, 280, 280FC or 282 prior to application of other finish coats. Refer to the applicable product data sheet for color availability and additional information.
||20 to 25 mils (508 to 635 microns) including fiberglass reinforcing mat.
If more than 24 hours have elapsed between coats, the coated surface must be mechanically abraded before topcoating.
|Temperature || To Topcoat || To Place in Service|
| 75°F (24°C) || 8-24 hours || 24 hours |
|Volatile Organic Compounds
||Unthinned: 0.16 lbs/gallon (19 grams/litre)
Thinned 5% (No. 2 Thinner): 0.52 lbs/gallon (63 grams/litre)
Thinned 5% (No. 42 Thinner): 0.50 lbs/gallon (60 grams/litre)
||1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates.
|Number of Components
||Three: Liquids Part A (epoxy) and Part B (amine)
Fiberglass Reinforcing Mat Part C (S273-0273C)