Series 27 | F.C. Typoxy

Generic Type Polyamide Epoxy
Common Usage Versatile low-temperature coating ideally suited for steel fabrication and OEM applications. Also widely used as a field tie-coat. Provides fast curing and rapid handling capabilities. Note: Series 27 conforms with air pollution regulations limiting Volatile Organic Compounds (VOC) to a maximum of 340 grams/litre (2.8 lbs/gal).
Colors Refer to Tnemec Color Guide. Note: Epoxies chalk with extended exposure to sunlight. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause yellowing to occur.
Finish Flat
Primers Steel: Self-priming or Series 1, 37H, 66, L69, L69F, N69, N69F, V69, V69F, 90, 94-H2O, 135, 394, 530
Galvanized Steel and Non-Ferrous Metal: Self-priming, Series 66 or L69, L69F, N69, N69F, V69, V69F.
Topcoats Series 2H, 30, 66, 73, 113, 114, 115, 175, 700, 701, 1028, 1029, 1070, 1071, 1072, 1074, 1075, 1077, 1078. Note: Series 27 exterior exposed for 3 weeks or longer requires an epoxy intermediate coat or scarification prior to topcoating with Series 2H. Refer to appropriate topcoat data sheet for additional information.
Volume Solids 58.0 ± 2.0% (mixed) †
Recommended DFT 2.0 to 6.0 mils (50 to 150 microns) per coat. Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.
Curing Time
Temperature To Touch To Handle To Recoat
75°F (24°C) 1/2 hour 2 hours 3 hours
65°F (18°C) 3/4 hour 4 hours 5-6 hours
55°F (11°C) 1 hour 4-5 hours 6-8 hours
45°F (7°C) 1-2 hours 6-8 hours 9-12 hours
35°F (2°C) 2-3 hours 9-12 hours 12-15 hours

Curing time varies with surface temperature, air movement, humidity and film thickness.
Volatile Organic Compounds Unthinned: 2.36 lbs/gallon (282 grams/litre)
Thinned 10% (No. 60 Thinner): 2.83 lbs/gallon (339 grams/litre)
Thinned 10% (No. 4 Thinner): 2.83 lbs/gallon (339 grams/litre) †
HAPS Unthinned: 2.59 lbs/gal solids
Thinned 10% (No. 60 Thinner): 2.59 lbs/gal solids
Thinned 10% (No. 4 Thinner): 3.54 lbs/gal solids
Theoretical Coverage 930 mil sq ft/gal (22.8 m²/L at 25 microns). See APPLICATION for coverage rates. †
Number of Components Two: Part A and Part B

The products listed below are not exact equivalents. They are only products that you may consider as alternatives in a general sense. Substrate type, condition, temperatures, surface preparation, primer/topcoat selection and intended use are just a few factors that will affect product selection. Please contact your local Tnemec Coatings Consultant for product recommendations.

This ProductPolyamide Epoxy
Volume SolidsRec. DFTV.O.C.# of Components
58.0 ± 2.0% (mixed) †2.0 to 6.0 mils (50 to 150 microns) per coat. Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.Unthinned: 2.36 lbs/gallon (282 grams/litre)
Thinned 10% (No. 60 Thinner): 2.83 lbs/gallon (339 grams/litre)
Thinned 10% (No. 4 Thinner): 2.83 lbs/gallon (339 grams/litre) †		Two: Part A and Part B
Series 135 | Chembuild Modified Polyamidoamine Epoxy
Hide this product's data
Volume SolidsRec. DFTV.O.C.# of Components
84.0 ± 2.0% (mixed) †Conventional Build: 4.0 to 6.0 mils (100 to 150 microns) per coat.
Hi-Build: 7.0 to 9.0 mils (180 to 230 microns) per coat.
Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.		EPA Method 24 Unthinned: 0.72 lbs/gallon (86 grams/litre)
Thinned 15% (No. 19 Thinner): 1.91 lbs/gallon (229 grams/litre)
Thinned 15% (No. 18 Thinner): 2.05 lbs/gallon (246 grams/litre)
Thinned 15% (No. 62 Thinner): 0.72 lbs/gallon (86 grams/litre) †		Two: Part A and Part B

Email this product

Typoxy was applied as the topcoat for the Boston University Ice Rink area.