Series 215 | Surfacing Epoxy

Generic Type Modified Polyamine Epoxy
Common Usage An advanced generation, 100% solids epoxy filler and surfacer for concrete or steel. Excellent material for surfacing, patching and filling voids and bugholes in concrete substrates. Generally topcoated with a variety of high performance epoxies and polyurethanes for use in mild to aggressive exposures.
Colors 1200 White, 1212 Gray
Finish Semi-Gloss
Surfacer/Filler/Patcher Self-patching or Series 217, 218
Primers Steel: Self-priming, Series 1, 20, FC20, 22, 66, L69, L69F, N69, N69F, V69, V69F, 90-97, H90-97, 90G-1K97, 91-H2O, H91-H2O, 94-H2O, L140, L140F, N140, N140F, V140, V140F, 161, 201, 394
Concrete: Self-priming, Series 20, FC20, 22, 66, L69, L69F, N69, N69F, V69, V69F, L140, L140F, N140, N140F, V140, V140F, 161, 201. Note: Primers may be necessary on some applications to minimize or eliminate the potential for outgassing.
CMU & Cement Board: Self-priming. Can also be used as a bedding coat for Series 273 Stranlok ML system.
Topcoats Series 20, FC20, 22, FC22, 61, 66, L69, L69F, N69, N69F, V69, V69F, 84, 104, 113, 114, 120, L140, L140F, N140, N140F, V140, V140F, 141, 161, 201, 270, 273, 280, 281, 282, 287, 406, 431, 434, 435, 436, 446.
Volume Solids 100% (mixed) †
Recommended DFT Resurfacer: 1/32” to 1/8” (0.8 mm to 3.2 mm)
Up to 2” with the addition of Series 211 (see Mixing instructions) for filling honeycombs, blow holes and surface imperfections found in formed concrete surfaces. Larger imperfections may require multiple applications. Bedding coat for mat lay up is typically in the 1/16" range.
Curing Time
Temperature To Touch Dry Through Maximum to Recoat ‡
95°F (35°C) 4 hours 12 hours 14 days
75°F (24°C) 10 hours 24 hours 21 days
55°F (13°C) 18 hours 48 hours 21 days
45°F (7°C) 24 hours 72 hours 21 days
35°F (2°C) 32 hours 96 hours 21 days
‡ Note: If the Series 215 surface is exterior exposed for more than seven days, scarification is required before topcoating.
Note: Use "To Touch" cure information for minimum recoat times if succeeding topcoats are spray-applied and "Dry Through" if succeeding topcoats are applied by roller, brush, or trowel.
Volatile Organic Compounds Unthinned: 0.08 lbs/gal solids (10 grams/litre) †
HAPS Unthinned: 0.0 lbs/gal solids
Theoretical Coverage 1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates. †
Number of Components Two: Part A and Part B (1 Part A to 1 Part B by volume)

The products listed below are not exact equivalents. They are only products that you may consider as alternatives in a general sense. Substrate type, condition, temperatures, surface preparation, primer/topcoat selection and intended use are just a few factors that will affect product selection. Please contact your local Tnemec Coatings Consultant for product recommendations.

This ProductModified Polyamine Epoxy
Volume SolidsRec. DFTV.O.C.# of Components
100% (mixed) †Resurfacer: 1/32” to 1/8” (0.8 mm to 3.2 mm)
Up to 2” with the addition of Series 211 (see Mixing instructions) for filling honeycombs, blow holes and surface imperfections found in formed concrete surfaces. Larger imperfections may require multiple applications. Bedding coat for mat lay up is typically in the 1/16" range.
Unthinned: 0.08 lbs/gal solids (10 grams/litre) †Two: Part A and Part B (1 Part A to 1 Part B by volume)
Series 218 | MortarClad Epoxy Modified Cementitious Mortar
Hide this product's data
Volume SolidsRec. DFTV.O.C.# of Components
100% (mixed)Parge Coat: 1/16”-1/4” per lift; maximum 1/2” thickness
Feather-edge Capable: 1/32”		Unthinned: 0.15 lbs/gallon (19 grams/litre)Three—Liquid: Part A and Part B Powder: Part C