||Glass Flake Reinforced Modified Polyamine Epoxy
||Abrasion resistant, high solids, epoxy coating which offers high-build edge protection and excellent corrosion resistance. Contains glass flake and aluminum oxide for improved film integrity. For use on the interior and exterior of steel or concrete tanks, pipes, and other heavy-duty equipment in industrial service.
||Available in the following standard industrial colors: A11417 Light Gray, 1252 Beige, 35GR Black. Note: Epoxies chalk with extended exposure to sunlight. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial stages of curing may cause yellowing to occur. Important: Due to the product's curing agent chemistry, color variations can be pronounced. However, these changes in color are aesthetic only and will not affect performance or certifications. Contact your Tnemec representative for more information.
||Series 215, 217, 218
||Steel: Self-priming, 1, L69, L69F, N69, N69F, 90E-92, 90G-1K97, 90-97, H90-97, 90G-98, 94-H2O
Concrete: Self-priming, L69, L69F, N69, N69F
||Exterior: Series 73, 290, 1028, 1029, 1074, 1074U, 1075, 1075U. Note: The following maximum recoat time applies when using Series 73, 290, 1074, 1074U, 1075, 1075U: fourteen (14) days. If this time limit is exceeded, Series 142 must be uniformly scarified prior to topcoating.
||82% ± 2.0% (mixed) †
||8.0 to 20.0 mils (205 to 500 microns) in one coat. Note: Thickness requirements will vary with substrate, application method and exposure. Contact your Tnemec representative.
Curing time varies with surface temperature, air movement, humidity and film thickness. ‡Note: Specific application requirements, including cure schedule and environmental conditions, must be followed when topcoating Series 142. Contact Tnemec Technical Service for detailed instructions. Note: For overlaps, tie-ins, and touch-ups, maximum recoat time with itself is seven days.
|Temperature||To Handle||To Topcoat||Immersion|
|75°F (24°C)||6 hours||9 hours ‡||7 days|
|35°F (0°C)||64 hours||72 hours ‡||30 days|
|Volatile Organic Compounds
||EPA Method 24
Unthinned: 1.28 lbs/gallon (153 grams/litre)
Thinned 5% (No. 4 Thinner): 1.55 lbs/gallon (186 grams/litre)
Thinned 5% (No. 60 Thinner): 1.55 lbs/gallon (186 grams/litre)
Thinned 10% (No. 4 Thinner): 1.78 lbs/gallon (214 grams/litre)
Thinned 10% (No. 60 Thinner): 1.74 lbs/gallon (208 grams/litre)†
||Unthinned: 1.27 lbs/gal solids
Thinned 5% (No. 4 Thinner): 1.31 lbs/gal solids
Thinned 10% (No. 4 Thinner): 1.36 lbs/gal solids
||1,315 mil sq ft/gal (32.2 m²/L at 25 microns). See APPLICATION for coverage rates. †
|Number of Components
||Two: Part A (amine) and Part B (epoxy)