Below is only a summary of product data. Please download the product datasheet for complete details. English: Product Data MSDS Spanish: Product Data MSDS French: Product Data MSDS
| Generic Type | Waterborne Acrylic Polyurethane | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Common Usage | A waterborne polyurethane coating that provides excellent abrasion resistance and color and gloss retention for exterior applications to steel, concrete and other miscellaneous substrates. It features low VOC content, low odor, semi-gloss finish and easy cleanup. | ||||||||
| Colors | Refer to Tnemec Color Guide. Note: Certain colors may require multiple coats depending on method of application and finish coat color. When feasible, the preceding coat should be in the same color family, but noticeably different. | ||||||||
| Finish | Semi-Gloss | ||||||||
| Primers | Steel: Series 20, 22, 27, 66, N69, N69F, L69, L69F, V69, V69F, 84, 104, 115, 135, L140, L140F, N140, N140F, V140, V140F, 141, 161, 287 Galvanized Steel and Non-Ferrous Metal: Series 66, L69, L69F, N69, N69F, V69, V69F, 115, 135, 161 Concrete: Series 20, 66, N69, N69F, L69, L69F, V69, V69F, 84, 104, 141, 161, 270, 273, 280, 287 CMU: L69, L69F, N69, N69F, V69, V69F, 130. Intermediate coat required (any of the above primers for concrete). Note: Epoxy primers exterior exposed for more than 30 days require an epoxy intermediate coat or scarification prior to topcoating with Series 1081. |
||||||||
| Intermediate | Series 35, 115, 287, 1028, 1029 | ||||||||
| Topcoats | Series 1080, 1088 | ||||||||
| Volume Solids | 61.0 ± 2.0% (mixed) † | ||||||||
| Recommended DFT | 2.0 to 3.0 mils (50 to 75 microns) per coat. Note: Application of coating below minimum or above maximum recommended dry film thicknesses may adversely affect coating aesthetics and performance. Number of coats and thickness requirements will vary with substrate, application method and exposure. Excessive film thicknesses will cause microbubbling. Contact your Tnemec representative. | ||||||||
| Curing Time |
Curing time varies with surface temperature, air movement, humidity and film thickness. |
||||||||
| Volatile Organic Compounds | Unthinned: 0.72 lbs/gallon (87 grams/litre) Thinned 5% (No. 66 Thinner): 1.22 lbs/gallon (147 grams/litre) † |
||||||||
| HAPS | Unthinned: 0 lbs/gal solids Thinned 15%: 0 lbs/gal solids |
||||||||
| Theoretical Coverage | 978 mil sq ft/gal (24.0 m²/L at 25 microns). See APPLICATION for coverage rates. † | ||||||||
| Number of Components | Two: Part A and Part B |
The walls and floors at the Northern California Animal Lab were coated with Series 1081 Endura-Shield to resist abrasion and retain the natural finishes of the substrates.