||A high-performance, fiberglass-reinforced wall coating for protection against acids, alkalis and physical abuse. Stranlok’s 100% solids epoxy technology is solventless and VOC compliant, making Stranlok virtually odorless and permitting application in occupied facilities. Its accelerated curing schedule and installation process mean faster return-to-service times. A unique blend of two types of premixed reinforcing fibers allows Stranlok to be spray or trowel applied up to 40 mils. The integrity of the interlocking fibers allows the surface to withstand daily high-pressure steam cleaning. In addition to this high tolerance to “thermal shock,” Stranlok also features broad chemical, impact and abrasion resistance.
||White. Note: Epoxies chalk and yellow with age, extended exposure to UV and artificial lighting. Lack of ventilation, incomplete mixing, miscatalyzation or the use of heaters that emit carbon dioxide and carbon monoxide during application and initial states of curing may cause amine blush, possibly affecting adhesion of subsequent topcoats.
||CMU, Concrete & Cement Board: Series 130, 215, 218, 1254. Series 201 mixed with fumed silica (refer to Technical bulletin 98-11). Refer to the applicable product data sheet for additional information. CMU or concrete must be filled or resurfaced with a recommended product prior to priming.
||Wood, Drywall & Pre-cast Concrete: Self-priming or Series 27WB, 201, 203
CMU: Series 201 over filled CMU
||Series 22, 27WB, 73, 84, 113, 114, 280, 282, 287, 290, 297, 1080, 1081. Note: Series 270 must be topcoated with 22, 27WB, 84, 280 or 282 prior to application of other finish coats.
||25 to 40 mils (635 to 1,015 microns) per coat.
Note: If more than 24 hours have elapsed between coats, the coated surface must be mechanically abraded before topcoating. † Note: Severe service may require a longer curing time. Contact your Tnemec representative or Tnemec Technical Services. Curing time varies with surface temperature, air movement, humidity and film thickness.
|Temperature || To Topcoat || To Place in Service † |
| 75°F (24°C) || 12-24 hours || 24 hours |
|Volatile Organic Compounds
||Unthinned: .02 lbs/gallon (3 grams/litre)
Thinned 3% (No. 42 Thinner): .22 lbs/gallon (26 grams/litre)
||1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates.
|Number of Components
||Two: Part A (epoxy) and Part B (amine)