Generic Type Modified Aliphatic Amine Epoxy Mortar
Common Usage A 100% solids, hybrid epoxy mortar designed for severe wastewater immersion and fume environments. Specifically formulated to withstand high levels of hydrogen sulfide gas (H2S), sulfuric acid (H2SO4), as well as other gases common to sewer exposures. Aggregate reinforcement provides additional resistance to abrasions and impacts.
Colors 5022 Beige
Surfacer/Filler/Patcher 215, 217, 218
Primers Concrete: Self-priming or Series 201
Topcoats Series 435
Volume Solids 100% (mixed)
Recommended DFT 1/8 inch or 125 mils (3,125 microns) minimum.
Curing Time
TemperatureTo TopcoatTo Place in ServiceMaximum Recoat
75°F (24°C) 8 hours 2 days 7 days
55°F (13°C) 12 hours 3 days 7 days
Note: Curing time will vary with surface temperature, air movement, humidity and film thickness. Note: If more than 7 days have elapsed between coats, the Series 434 coated surface must be mechanically abraded before topcoating.
Volatile Organic Compounds EPA Method 24: 0.15 lbs/gallon (18 grams/litre)
HAPS 0.06 lbs/gal solids
Theoretical Coverage 1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates.
Number of Components Three: Part A (Amine), Part B (Epoxy) and Part C (Aggregate)